Fracture Toughness / Fracture Energy Data for Oxide Glass

NIST Standard Reference Database 137


Borate Base Glassess

Reference:

Other material collections: Property Data Summaries

Other materials: Oxide Glasses


Other Borate Glasses materials

B2O3 Base Glasses: B40f

Material Summary:

Molar composition: 40% B2O3 + 45% PbO + 15% ZnO

Property Summary:

Property                           Value  Environment  Notes
---------------------------------  -----  -----------  --------------------------------------
Crack Growth Exponent []   .......: 
Elastic Modulus [GPa]   ..........: 69.8   N2 liquid   
Fracture Energy [J/m2]  ..........:  1.66  N2 liquid  Controlled flaw 
Fracture Toughness [MPa m1/2].....:  0.48  N2 liquid  Controlled flaw 
Crack Growth Exponent []   .......:
Elastic Modulus [GPa]   ..........: 69.8   Air     
Fracture Energy [J/m2]  ..........:  1.30  Air          Controlled flaw
Fracture Toughness [MPa m1/2].....:  0.43  Air          Controlled flaw