Fracture Toughness / Fracture Energy Data for Oxide Glass

NIST Standard Reference Database 137


Germanate Base Glasses

Reference:

Other material collections: Property Data Summaries

Other materials: Oxide Glasses



Other Germanate Glasses materials

GeO2 Base Glasses: G90b

Material Summary:

Molar composition: 90% GeO2 + 10% K2O

Property Summary:

Property                           Value  Environment  Notes
---------------------------------  -----  -----------  --------------------------------------
Crack Growth Exponent []   .......:  
Elastic Modulus [GPa]   ..........: 60.31  N2 gas     
Fracture Energy [J/m2]  ..........:  4.4   N2 gas     Notched beam,precracked
samples,
                                                       crosshead speed 4.3 µm/s,dew point 50 °C
Fracture Toughness [MPa m1/2].....:  0.75  N2 gas     Notched beam,precracked samples,
                                                       crosshead speed 4.3 µm/s,dew point 50 °C