NIST Standard Reference Database 137
Other material collections: Property Data Summaries
Other materials: Oxide Glasses
Other Silicate Glasses materials
Property Value Environment Notes --------------------------------- ----- ----------- -------------------------------------- Crack Growth Exponent [] .......: Elastic Modulus [GPa] ..........: 89.0 N2 liquid Fracture Energy [J/m2] ..........: 7.0 N2 liquid Double cantilever beam Fracture Toughness [MPa m1/2].....: 1.12 N2 liquid Double cantilever beam Crack Growth Exponent [] .......: 21 D.I. H2O Double cantilever beam Elastic Modulus [GPa] ..........: Fracture Energy [J/m2] ..........: Fracture Toughness [MPa m1/2].....: Crack Growth Exponent [] .......: 21 IM Cs in Double cantilever beam D.I. H2O Elastic Modulus [GPa] ..........: Fracture Energy [J/m2] ..........: Fracture Toughness [MPa m1/2].....: Crack Growth Exponent [] .......: 30 IM Cs in Double cantilever beam D.I. H2O Elastic Modulus [GPa] ..........: Fracture Energy [J/m2] ..........: Fracture Toughness [MPa m1/2].....: Crack Growth Exponent [] .......: 93 Air, 30% RH Double cantilever beam Elastic Modulus [GPa] ..........: Fracture Energy [J/m2] ..........: Fracture Toughness [MPa m1/2].....: