Fracture Toughness / Fracture Energy Data for Oxide Glass

NIST Standard Reference Database 137


Silicate Base Glasses

Reference:

Other material collections: Property Data Summaries

Other materials: Oxide Glasses


Other Silicate Glasses materials

SiO2 Base Glasses: S56c

Material Summary:

Molar composition: 56% SiO2 + 24% Al2O3 + 20% Na2O

Property Summary:

Property                           Value  Environment  Notes
---------------------------------  -----  -----------  --------------------------------------
Crack Growth Exponent []   .......: 
Elastic Modulus [GPa]   ..........: 77.5   Air          
Fracture Energy [J/m2]  ..........:  2.85  Air          Notched beam
Fracture Toughness [MPa m1/2].....:  0.67  Air          Notched beam