IUPAC-NIST Solubility Database
NIST Standard Reference Database 106
Solubility System:
Carbon dioxide with Cellulose acetate (CA)
Components:
(1) Carbon dioxide; CO2; [124-38-9]
NIST Chemistry WebBook
for detail
(2) Cellulose acetate (CA); ; [9004-35-7]
NIST Chemistry WebBook
for detail
Original Measurements:
E. Sada, H. Kumazawa, Y. Yoshio, S.-T. Wang and P. Xu, J. Polym. Sci., Part B: Polym. Phys. 26, 1035 (1988).
Variables:
Temperature = 293 K - 313 K
Pressure = 293 K - 313 K
Prepared By:
Yu. P. Yampol'skii
Experimental Data:
(Subscripts 1,2,3, ..., in column headings refer to components 1,2,3, ...)
Dual mode sorption parameters for carbon dioxide in cellulose acetate
T/K
Henry's law constant, K [cm
3
(STP)/cm
3
atm]
Langmuir's parameter, C
H
[cm
3
(STP) cm
-3
]
Affinity Coefficient b [atm
-1
]
293
1.83
22.7
0.500
302
1.24
20.3
0.437
313
1.10
17.7
0.280
View Figure 1 for this Evaluation
Notes:
*
delta;
H
H
= 22.7 kJ/mol; delta
H
D
= 17.8 kJ/mol.
Method/Apparatus/Procedure:
Sorption was measured by the pressure decay method. The procedure and apparatus were similar to those described in Ref. 1.
Source and Purity of Materials:
CA: Eastman Kodak (E 398-3); content of acetyl groups 39.8 %. The film cast from acetone solution was annealed in a water bath at 363 K for 10 min. The film was dried in vacuum for 24 h before measurement of sorption.
Estimated Errors:
Temperature: No information given.
References:
1
W. J. Koros, D. R. Paul, and A. A. Rocha, J. Polym. Sci., Polym. Phys. Ed. 14, 667 (1976).