IUPAC-NIST Solubility Database
NIST Standard Reference Database 106
Solubility System:
Carbon dioxide with Hexafluorpolycarbonate (HFPC)
Components:
(1) Carbon dioxide; CO2; [124-38-9]
NIST Chemistry WebBook
for detail
(2) Hexafluorpolycarbonate (HFPC); ; [32291-26-2]
NIST Chemistry WebBook
for detail
Original Measurements:
G.K. Fleming and W.J. Koros, J. Polym. Sci., Part B: Polym. Phys. 28, 1137 (1990).
Variables:
Temperature = 308 K
Pressure = 308 K
Prepared By:
V.I. Bondar
Experimental Data:
(Subscripts 1,2,3, ..., in column headings refer to components 1,2,3, ...)
Table 1. Sorption and desorption isotherms of carbon dioxide in HFPC at 308 K (The original data were represented graphically)
Pressure [MPa]
Solubility [(V*
1
(STP)/V*
2
)]
Remark(s)
0.59
30.19
Sorption
0.88
36.46
Sorption
1.20
42.07
Sorption
1.54
46.17
Sorption
1.83
49.61
Sorption
2.08
52.41
Sorption
2.23
53.70
Sorption
2.39
54.99
Sorption
2.63
57.14
Sorption
2.89
59.07
Sorption
3.12
60.57
Sorption
3.29
61.42
Sorption
0.32
13.48
Desorption
0.69
20.83
Desorption
1.03
26.23
Desorption
1.37
30.76
Desorption
1.63
36.60
Desorption
1.91
40.70
Desorption
2.11
43.72
Desorption
2.37
47.82
Desorption
2.60
51.28
Desorption
2.77
53.43
Desorption
2.94
56.24
Desorption
3.09
58.40
Desorption
3.29
61.42
Desorption
Table 2. Sorption isotherms of carbon dioxide in HFPC at 308 K in fugacity basis (The original data were represented graphically)
Sorption [(V*
1
(STP)/V*
2
)]
Fugacity [MPa]
16.40
0.36
26.28
0.72
33.42
1.08
38.05
1.36
42.04
1.63
45.62
1.85
49.40
2.11
52.97
2.32
55.92
2.52
58.65
2.68
61.38
2.82
Table 3. Dual mode sorption parameters for carbon dioxide in HFPC at 308 K
Henry's law constant, K [cm
3
(STP) cm
-3
atm
-1
]
Langmuir's parameter, C
H
[cm
3
(STP) cm
-3
]
Affinity Coefficient b [atm
-1
]
Remark(s)
1.09
28.05
0.255
Type: Pressure
1.33
25.48
0.275
Type: Fugacity
Method/Apparatus/Procedure:
Pressure decay sorption cell and procedure were described in Ref. 1.
Source and Purity of Materials:
HFPC: Dow Chemical Co., density 1.478 g/cm
3
, glass transition temperature 445 K,
d
spacing 5.8 A (WAXD method). The polymer was conditioned before measurement of sorption isotherms by exposing to CO
2
at 33 atm.
Estimated Errors:
Temperature: No information given.
References:
1
G. K. Fleming and W. J. Koros, Macromolecules 19, 2285 (1986).